软包装粘合剂用DOW美国陶氏 AMPLIFY TY 1354 马来接枝酸酐MAH

AMPLIFY™ TY 1354
Functional Polymer
陶氏塑料
产品说明
AMPLIFY™ TY 1354 Functional Polymer is a maleic anhydride grafted (MAH) polymer. In tie layers for flexible packaging, AMPLIFY TY 1354 Functional Polymer promotes 
adhesion of Polyethylene to barrier polymers such as polyamide and other polar substrates.
Main Characteristics:
Excellent adhesion to polyamide
Excellent physical properties
Wide range of process and service temperature
For blown and cast film
Complies with:
US FDA 21 CFR 175.105 (c)(5)
EU, No 10/2011
Consult the regulations for complete details.
基本信息
机构评级 FDA 21 CFR 175.105 欧洲 No 10/2011
形式 粒子
物理性能 额定值 单位制 测试方法
密度 0.920 g/cm³ ASTM D792 
熔流率(熔体流动速率) (190°C/2.16 kg) 3.0 g/10 min ASTM D1238, ISO 1133 
MAH 接枝水平 1
Low 内部方法
薄膜 额定值 单位制 测试方法
膜耐刺穿性 (51 µm) 9.51 J/cm³ 内部方法
割线模量 ASTM D882 
2% 正割, MD : 51 µm 214 MPa ASTM D882 
2% 正割, TD : 51 µm 240 MPa ASTM D882 
抗张强度 ASTM D882 
MD : 屈服, 51 µm 11.2 MPa ASTM D882 
TD : 屈服, 51 µm 11.5 MPa ASTM D882 
MD : 断裂, 51 µm 35.2 MPa ASTM D882 
TD : 断裂, 51 µm 31.2 MPa ASTM D882 
伸长率 ASTM D882 
MD : 断裂, 51 µm 730 % ASTM D882 
TD : 断裂, 51 µm 750 % ASTM D882 
落锤冲击 (51 µm) 210 g ASTM D1709 
埃尔曼多夫抗撕强度 2
ASTM D1922 
MD : 51 µm 890 g ASTM D1922 
TD : 51 µm 1100 g ASTM D1922 
热性能 额定值 单位制 测试方法
维卡软化温度 98.9 °C ASTM D1525 
溶融温度(DSC) 123 °C 内部方法
光学性能 额定值 测试方法
光泽度 (45°, 50.8 µm) 66 ASTM D2457 
挤压说明
Recommended Melt Temperature - 400-446°FFabrication Conditions for Blown Film
Screw Size: 2.5 in. (63.5 mm); 24:1 L/D
Screw Type: Barrier screw
Die Gap: 70 mil (1.8 mm)
Melt Temperature: 430°F (221°C)
Output: 6 lb/hr/in of die circumference
Die diameter: 6 in
Blow-Up Ratio: 2.5:1
Screw Speed: 70 rpm
备注
1. Low: 0.5 wt%
2. Method B